Flexible Packaging for Your Product

Structure Example: Main Functions and Features; BOPP/PE: Economical and practical, moisture-proof, heat-sealable; PET/VMPET/PE: High barrier, metallic luster, storage-resistant; PET/AL/CPP: Ultra-high barrier, light-shielding, high-temperature resistant; PET/AL/PA /CPP: Extremely strong toughness, puncture-resistant, steaming-resistant

Type: Description and Advantages; Standard suction bag: The suction nozzle is installed at the top corner of the bag, which is the most common type. It is convenient for pouring and easy to control.; Inclined nozzle bag: The suction nozzle is installed at a certain angle, making the pouring more in line with human engineering, and enabling a more thorough emptying of the contents.; Flat suction bag: The suction nozzle is designed to be wider and flatter, making it convenient for pouring thick liquids or sauces containing solids.; Zippered suction bag: Combines the functions of the suction nozzle and the zipper closure. The suction nozzle is used for pouring, and the zipper is used for long-term sealing and preservation.

Features: Four-sided sealing bag; Number of sealing edges: Four (top, bottom, left, right); Appearance structure: The quad seal pouch is more like a flat pillow or envelope, with a back sealing; Printing area: Two independent and complete printing surfaces, with excellent effect; Cost: Slightly higher, due to more sealing edges, the material utilization rate is slightly lower; Common applications: Pet food, heavy materials, high-end snacks, products requiring the best printing effect.

Type: Description; Three-side sealed bag: The most common type, with sealed edges on the back and both sides; Stand up pouch with zipper: With a flat bottom design at the bottom and a zipper at the bag opening, this kind of transparent pouch can be repeatedly sealed.; Flat Bottom bag: All four sides can stand upright, providing a larger display area and a more three-dimensional appearance.; Vacuum bag: Sealed after removing air, effectively preventing product oxidation and deterioration.; Shrinking bag: After heating, this type of transparent pouch will tightly adhere to the product and perfectly display the product outline.; Special-shaped bags: Designed in special shapes, such as hand-held type, mouth-type, etc.

Type: Description and Advantages; Self-standing Zipper Bag: The bottom is straight, allowing it to stand independently on the shelf. This kind of zipper pouch packaging offers the best shelf display effect and is the preferred choice for brand marketing.; Three-side Sealed Zipper Bag: The most common economical bag type, with the back and both sides sealed. This type of zipper pouch packaging is cost-effective and widely applicable.; Vacuum Zipper Bag: The bag body is made of high-barrier material and equipped with a special one-way exhaust valve. After the air is removed, this form of zipper pouch packaging achieves vacuum sealing and has excellent preservation effect.; Special-shaped and Spout Zipper Bag: This kind of zipper pouch packaging enhances functionality and attractiveness through unique designs (such as special-shaped contours, attached spouts or screw caps).

Material structure: Kraft paper / PET /CPP or other; Color: Kraft paper brown / white; Tear notches: With Tear notches; Valve: With/ without Valve; Viewing window: With/ without viewing window; Zip-closure: With zip-closure; Suction nozzle: with / without spout; Barrier properties: Middium; Size recommendations: 100ml : 85 x 140mm +50mmBG 250ml :110 x 185mm +65mmBG 500ml : 130 x 225mm +70mmBG750ml : 160 x 270mm +80mmBG1L: 180 x 290mm +90mmBG2L:  210 x 310mm +110mmBG3L: 250 x 340mm +130mmBG5L:300 x 370mm +160mmBG; Remark: customized services can be provied as per clients' specific requirement.

Product Name: MDOPE25; Testing Item: Unit; Thickness: μm; Average Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Wetting Tensioning: treated side; untreated side: mN/m; C.O.F: /; Haze: %; Gloss ( 60°∠）: /; Heat sealing strength: N/15mm

Feature: Benefit & Explanation; Self-Standing Ability: Superior Shelf Presence: The plastic stand-up pouch stands upright like a rigid package, making products more visible and attractive to consumers.; Lightweight & Flexible: Cost-Effective Logistics: The plastic stand-up pouch weighs much less than rigid alternatives, significantly reducing shipping costs. Empty plastic stand-up pouches lie flat, saving storage space.; Excellent Sealability: Content Protection: The plastic stand-up pouch provides a hermetic seal (via heat sealing) to protect against leakage, moisture, and contamination.; Large Printable Surface Area: Powerful Marketing Canvas: The plastic stand-up pouch offers ample, high-quality space for vibrant graphics and branding, acting as a billboard for the product.; High Functional Versatility: Enhanced User Convenience: The plastic stand-up pouch can be easily equipped with resealable zippers, easy-tear notches, and dispensing spouts for improved usability.

Product Name: CPP  film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Initial Sealing Temperature: ℃; Heat Sealing Strength: N/15mm; Haze: %; Wetting Tension: Treated; Untrested: mN/cm

Product Name: Inflatable CPP  film; Testing Item: Unit; Basic CPP: High Gloss & Transparent CPP; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; C.O.F.   (untreated side): -; Heat Sealing Strength: N/15mm; Haze: %; Wetting Tension: Treated

Product Name: Easy Peel  PE  Film; Testing Item: Unit; low strength: Medium-high strength; Thickness: μm; Tensile Strength: MD; TD: N/15mm; Elongation at break: MD; Right-angle tear: MD; Heat seal strength (125℃）: MD; Wetting Tension: Treated side; C .O. F.: Non Corona

Product Name: RCPP film; Testing Item: Unit; regular 121℃: High 135℃; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; C.O.F. (untreated side): -; Heat Sealing Strength: N/15mm; Haze: %; Wetting Tension: Treated side

Product Name: VMPE Film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Al thickness: O.D.; Aluminum Layer adhesion: N; Heat seal: N/15mm; Wetting Tension: mN/cm; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Product Name: Nylon co-extrusion Film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Wetting Tension: mN/cm; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Product Name: Low initial temperature CPP  film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Initial Sealing Temperature: ℃; Heat Sealing Strength: N/15mm; Haze: %; Wetting Tension: Treated; Untrested: mN/cm

Product Name: CPE Film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Wetting Tension: Treated side; Heat seal temperature: ℃; Heat seal strength: N/15mm; Haze: %

Product Name: EVOH co-extrusion Film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Wetting Tension: mN/cm; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Product Name: BOPP film; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Heat shrinkage: MD; Haze: %; Gloss 60°: %; Wetting Tension: Treated; Untrested: mN/cm

Product Name: VMCPP 35mic; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: Mpa; Aluminum Layer adhesion: N/15mm; Heat Sealing Strength: N/15mm; Optical Density: /; Wetting Tension: mN/cm; C.O.F.: /; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Product Name: 25mic AMDOPE; Testing Item: Unit; Thickness: μm; Density: g/m³; Tensile Strength: MD; TD: %; Elongation at break: MD; C.O.F: μs; μk: /; Wetting Tension: mN/cm; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Product Name: Matt BOPP; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Heat shrinkage: MD; Haze: %; Gloss  45°: %; C.O.F.: Treated side; Untreated side: -; Wetting Tension: Treated side

Product Name: 25mic ABOPE; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; C.O.F: μs; μk: /; Wetting Tension: mN/cm; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Properties: BOPE (Biaxially Oriented Polyethylene); Strength and toughness: Excellent, with good impact resistance and puncture resistance; Rigidity: High; Water vapor barrier: Excellent water vapor barrier; Heat sealing performance: Excellent, with a wide heat sealing temperature range and high strength; Transparency: Extremely high; Sustainability: Recyclable from the base material (belongs to the PE family); Product Name: BOPE25; Testing item: Unit; Thickness: μm; Average Thickness: μm; Tensile Strength: MD; TD: ≤7.0; Tensile Elongation: MD; Heat Shrinkage: MD; C.O.F: μs; Out side/Out side: μd; Gloss 60°: %; Haze: %; Dart impact Strength: g; Surface Tension: Corona; Out side: ≤32

Product Name: Heat seal BOPP; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Heat shrinkage: MD; Haze: %; Gloss  45°: %; Heat Seal Strength (125℃）: N/15mm; C.O.F.: Treated side; Untreated side: -; Wetting Tension: Treated side

Product Name: 19mic ABOPP; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; C.O.F: μs; μk: /; Wetting Tension: mN/cm; O2TR: cm3/m2.d.0.1Mpa; WVTR: g/m2.d

Characteristic /Description: Heat Sealable BOPE Film; Basic Definition: A biaxially oriented polyethylene film with heat sealing functionality, typically produced through co-extrusion blow molding or coating processes.; Core Features: High strength, high transparency, excellent puncture resistance, outstanding low-temperature toughness, and superior heat sealing performance.; Main Advantages: Simplifies packaging structure, facilitates recycling, reduces thickness and emissions, enhances packaging efficiency, and lowers the rate of package breakage.; Typical Applications: Food packaging, daily necessities packaging, cold chain logistics, pharmaceutical packaging, electronic product packaging, etc.; Product Name: 25mic Heat seal BOPE; Testing item: Unit; Thickness: μm; Average Thickness: μm; Tensile Strength: MD; TD: ≤4.0; Tensile Elongation: MD; Heat Shrinkage: MD; C.O.F: μs; Out side/Out side: μd; Gloss 45°: %; Haze: %; Heat Seal Strength (95℃）: N/15mm; Surface Tension: Treated side

Product Name: Anti-Fog  BOPP; Testing Item: Unit; Thickness: μm; Tensile Strength: MD; TD: %; Elongation at break: MD; Heat shrinkage: MD; Haze: %; Gloss  45°: %; Heat Seal Strength (125℃）: N/15mm; C.O.F.: Treated side; Untreated side: -; Wetting Tension: Treated side

Characteristic: VMBOPP; Material properties: Stiff, high in strength, stable in size; Core advantage: Balanced overall performance, high cost-effectiveness.; Heat Sealing Performance: Poor (requires laminating); Typical application: Middle layer or outer layer of packaging